Abstract:The dust generated during chlorination process in recovering titanium by metallurgical process was washed with water. Then, the residue left after water-washing was subjected to calcification roasting process, and the effects of roasting temperature and roasting time on the leaching rate of vanadium from the residue were studied. The results indicate that vanadium in the dust from chlorination process mainly exists as low-valent vanadium, and the vanadium leaching rate increases with the rising temperature. The vanadium leaching rate reaches 88% with the roasting temperature of 850 ℃. As the roasting time increases, the previously obtained different products undergo a secondary reaction, forming insoluble compounds of vanadium bronze, and also vanadate with different valences, which results in different vanadium leaching rates in Na2CO3 solution. It is concluded that the roasting process should be optimally at temperature of 850 ℃ with a roasting time of 120 minutes.
金春容, 贺永东, 赵亿坤, 孙小涵, 杜玉峰, 白万全, 陈守俊, 刘小龙. 钛冶金氯化收尘渣钒资源回收利用研究[J]. 矿冶工程, 2024, 44(1): 89-94.
JIN Chunrong, HE Yongdong, ZHAO Yikun, SUN Xiaohan, DU Yufeng, BAI Wanquan, CHEN Shoujun, LIU Xiaolong. Recovery and Utilization of Vanadium Resources in Dust from Chlorination Process for Recovering Titanium. Mining and Metallurgical Engineering, 2024, 44(1): 89-94.
[1] ZHANG J, ZHANG W, ZHANG L, et al. Mechanism of vanadium slag roasting with calcium oxide[J]. International Journal of Mineral Processing, 2015,138:20-29.
[2] ZHANG J, ZHANG W, XUE Z. An environment-friendly process featuring calcified roasting and precipitation purification to prepare vanadium pentoxide from the converter vanadium slag[J]. Metals, 2018,9(1):21.
[3] LI H Y, WANG K, HUA W H, et al. Selective leaching of vanadium in calcification-roasted vanadium slag by ammonium carbonate[J]. Hydrometallurgy, 2016,160:18-25.
[4] ZHU F, MA S, MA Z, et al. Preparation of TiCl4 from panzhihua ilmenite concentrate by boiling chlorination[J]. Journal of Materials Researchand Technology, 2023,23:2703-2718.
[5] DU G, LI Z, ZHANG J, et al. Chlorination behaviors for green and efficient vanadium recovery from tailing of refining crude titanium tetrachloride[J]. Journal of Hazardous Materials, 2021,420:126501.
[6] 田 键,张 祥,黄季宇,等. 沸腾氯化生产TiCl4工艺分析及氯化废料的综合利用[J]. 钛工业进展, 2018,35(3):6-10.
[7] 王海北,邹小平,谢 铿,等. 典型固废资源化与无害化处置技术[J].有色金属(冶炼部分), 2022(9):1-8.
[8] 郝峰焱,祝 星,祁先进,等. 钢渣改性对污酸除砷的影响[J]. 中国有色金属学报, 2020,256(7):1703-1714.
[9] 李学鹏,王 娟,常 军,等. 砷铁渣中砷和铁的资源化利用研究[J].矿冶工程, 2023,43(2):105-108.
[10] XIANG J Y, WANG X, PEI G S, et al. Recovery of vanadium from vanadium slag by composite roasting with CaO/MgO and leaching[J].Transactions of Nonferrous Metals Society of China, 2020,30(11):3114-3123.
[11] SONG W C, LI H, ZHU F X, et al. Extraction of vanadium from molten vanadium bearing slag by oxidation with pure oxygen in the presence of CaO[J]. Transactions of Nonferrous Metals Society of China, 2014,24(8):2687-2694.
[12] 王少娜,吕页清,刘 彪,等. 钒渣亚熔盐法钒铬共提工艺清洁生产评价[J]. 中国有色金属学报, 2021,31(3):736-747.
[13] LI M, LIU S, ZHANG Z. Dual guided loss for ground-based cloud classification in weather station networks[J]. IEEE Access, 2019,7:63081-63088.
[14] ZHANG G, WANG K, LUO M. Mechanism on the separation of vanadium and titanium from vanadium slag by roasting with ammonium sulfate[J]. Separations, 2022,9(8):196.