Abstract:Experiments were conducted on the process of pressure acid leaching of steelmaking dust from galvanized sheet scrap, which were compared with normal pressure acid leaching process for investigating the effects of initial concentration of sulfuric acid, leaching time, liquid to solid ratio, as well as temperature on the leaching rate. Results showed that the pressure leaching technique can result in both zinc ferrite that is insoluble in weak acid at the normal temperature and refractory zinc silicate effectively leached. It is found that the leaching process at temperature of 140 ℃ for 1.5 h in the reactor with pressure kept at 0.6 MPa, with liquid to solid ratio at 6∶1, rotating at 500 r/min, concentration of sulfuric acid at 120 g/L, resulted in the leaching rate of zinc and iron at 98.35% and 3.51%, respectively, with almost all lead into the slag phase. The silicon content in the leaching liquid is only 0.06 g/L, indicating an effective separation between zinc and impurities in the dust.
贺山明, 汪金良, 李啊林, 曹才放, 杨亮. 废镀锌板炼钢粉尘加压硫酸浸出试验研究[J]. 矿冶工程, 2016, 36(2): 84-87.
HE Shan-ming, WANG Jin-liang, LI A-lin, CAO Cai-fang, YANG Liang. Experimental Study on Pressure Acid Leaching of Steelmaking Dust from Galvanized Sheet Scrap. Mining and Metallurgical Engineering, 2016, 36(2): 84-87.
[1] Jha M K, Kumar V, Singh R J. Review of hydrometallurgical recovery of zinc from industrial wastes[J]. Resources Conservation and Recycling, 2001,33(1):1-22.
[2] Kelebek S, Yoruk S, Davis B. Characterization of basic oxygen furnace dust and zinc removal by acid leaching[J]. Minerals Engineering, 2004,17(2):285-291.
[3] 郭玉华,张春霞,上官方钦,等. 中国废旧镀锌钢板中的锌资源量[J]. 钢铁,2014,49(2): 69-73.
[4] 舒 波,范兴祥,黄 卉,等. 从热滤渣中富集贵金属的实验研究[J]. 矿冶工程, 2015(1):103-106.
[5] 孙红燕,森 维,肖锐敏. 机械活化铅锌烟尘强化硫酸浸出的工艺研究[J]. 矿冶工程, 2014(3):97-99.
[6] Reyad A Shawabkeh. Hydrometallurgical extraction of zinc from Jordanian electric arc furnace dust[J]. Hydrometallurgy,2010(1):61-65.
[7] 徐 瑞,杨丽梅,黄松涛,等. 三明炼钢粉尘的基本物性及酸浸回收锌的实验研究[J]. 过程工程学报,2013,13(1): 48-54.
[8] Havlík Tomás, Vidore Souza Bruna, Bernardes Andrea Moura, et al. Hydrometallurgical processing of carbon steel EAF dust[J]. Journal of Hazardous Materials, 2006(1-3):311-318.
[9] 李 岩,徐 政,王 巍,等. 两种废镀锌板炼钢烟尘的联合浸出[J]. 有色金属工程,2013,3(4): 49-51.
[10] 梅光贵,王德润,周敬元,等. 湿法炼锌学[M]. 长沙: 中南大学出版社,2001.
[11] 王吉坤,周廷熙. 硫化锌精矿加压酸浸技术及产业化[M]. 北京: 冶金工业出版社,2005.
[12] 贺山明,王吉坤,汪金良,等. 硅酸锌加压硫酸浸出的热力学分析与实验研究[J]. 过程工程学报,2014,14(6): 930-936.